| ✓ Ideally suited. |
X Not suited. |
| Processing caracteristics |
| Wood training |
✓ |
| Sandable |
✓ |
| Polishable |
✓ |
| Max. Pouring height per process1 |
1cm |
| Waiting time until further casting2 |
6h |
| Gelling time and pot life for 100g |
25min.
|
| Min. processing temperature |
15°C |
| Recommended processing temperature |
20°C |
| Max. relative humidity during processing |
70% |
| Max. material shrinkage |
1% |
| Processing time (at 20°C) |
| At layer height 0-3mm |
60min. |
| At layer height 1cm |
25min. |
| At layer height 2cm |
X |
| At layer height 5cm |
X |
| Technical properties |
| Touchable / Accessible after |
24h |
| Completely chemical cured after |
7 days |
| Transparent resin |
✓ |
| Crystal clear curing |
X |
| Max. possible UV protection3 |
X |
| Self-venting |
✓ |
| Bubble free |
✓ |
| Self-leveling |
✓ |
| Solvent-free |
✓ |
| VOC free4 |
X |
| BPA free5 |
✓ |
| Plasticizer free (Phthalate) |
✓ |
| Resistant to chemicals |
✓ |
| Scratch resistant6 |
✓ |
| Doming effect (depth effect) |
✓ |
| Miscible with all EPODEX colors (except WB PIGMENT) |
✓ |
| Suitable for underfloor heating |
✓ |
| Suitable for outdoor use |
X |
| High adhesion |
✓ |
| Density (g/cm3) |
1.1 |
| Viscosity (mPa·s) |
700 |
| Max. heat deflection temperature7 |
60°C |
| Min. heat deflection temperature |
-30°C |
| SHORE hardness after curing (D1) |
87 |
| Storage temperature |
10-30°C |
| Shelf life |
12 months |
| Shelf life after opening8 |
6 months |
- Casting above the maximum pouring height per process is not recommended. The resin may boil as a result of the reaction and yellowing, cracking and deformation can occur. By reducing the temperature (room, substrate, material temperature to e.g. 15 °C and reducing the area to e.g. 10x10cm, casting heights of up to 30cm can be achieved in one casting process.
- There is no maximum time limit to pour the next layer.
- No epoxy resin is completely UV resistant. However, high-quality raw materials and additives such as UV absorbers can increase UV protection. By using a topcoat, you can increase UV resistance even further. Possible topcoats are e.g. transparent polyurethane (PU) resins or lacquers which are painted or sprayed onto the epoxy coating as a finish.
- When properly used and completely cured, it is VOC free.
- According to formula without free BPA.
- Our epoxy resin systems have a high scratch resistance, but are not completely scratch-resistant. Scratch resistance can be increased by using a topcoat. Possible topcoats are e.g. transparent polyurethane (PU) resins or lacquers which are painted or sprayed onto the epoxy coating as a finish.
- The heat deflection temperature indicates up to which temperature the cured epoxy resin system remains mechanically stable. At higher temperatures, the cured epoxy can soften. By annealing (curing at higher temperatures >60°C), the heat resistance can be increased.
- If the lid of the container is closed directly after opening, the shelf life after opening is at least 6 months.